Trial production of titanium orthodontic brackets fabricated by metal injection molding (MIM) with sintering.
Safety and esthetics are two indispensable factors to consider when fabricating orthodontic brackets. However, these factors are not easily achieved when conventional techniques (including forging and casting) are used in the mass production of titanium brackets, albeit the brackets exhibit excellent biocompatibility. In the present study, orthodontic brackets were manufactured by metal powder injection molding with sintering. Brackets with three different base designs were made and subjected to compression shear tests for evaluation of their bonding strength to enamel substrate. The shapes given to the dimple of the base were spherical, oval, and grooved. The maximum shear forces for each type were 11.1 kgf, 7.6 kgf, and 18.5 kgf, respectively. The bonding strengths of the titanium bracket were equivalent to those obtained with conventional stainless steel brackets. Moreover, uniform distribution of Vickers hardness values (average, 240 +/- 40 Hv) measured at three locations indicated that the titanium bracket was uniformly sintered. Accordingly, titanium brackets thus fabricated exhibit a potential for clinical application.[1]References
- Trial production of titanium orthodontic brackets fabricated by metal injection molding (MIM) with sintering. Deguchi, T., Ito, M., Obata, A., Koh, Y., Yamagishi, T., Oshida, Y. J. Dent. Res. (1996) [Pubmed]
Annotations and hyperlinks in this abstract are from individual authors of WikiGenes or automatically generated by the WikiGenes Data Mining Engine. The abstract is from MEDLINE®/PubMed®, a database of the U.S. National Library of Medicine.About WikiGenesOpen Access LicencePrivacy PolicyTerms of Useapsburg