Della Bona, A. et al.

Shear bond strength of resin bonded ceramic after different try-in procedures.

Final cementation of porcelain laminate veneers may require a previous colour match try-in. The purpose of this in vitro study was to evaluate the effect on shear bond strength of resin bonded to porcelain after the application of different try-in procedures. Forty porcelain specimens were fabricated, flattened with 600 grit SiC, etched with hydrofluoric acid and silane treated. After 24 h the specimens were divided into four groups at random and prior to bonding of a dual cure resin composite button were treated as follows: Group 1, no treatment (control); Group 2, non-activated resin applied for 5 min, cleaned in acetone for 3 min; Group 3, as for Group 2, with silane reapplied; Group 4, as for group 3, but re-etched for 30 s before reapplication of silane. After bonding the specimens were stored in water at room temperature for 7 days. Shear bond strength data were as follows: Group 1, 18.6 +/- 1.6; Group 2, 15.9 +/- 1.7; Group 3, 16.7 +/- 2.6; Group 4, 15.3 +/- 3.0 MPa. Fractured surfaces examined, under light microscopy and scanning electron microscopy (SEM), showed cohesive failure within the porcelain in all cases. The reduction in mean bond strength after application of a try-in resin was significant in Groups 2 and 4 compared with the control (ANOVA P < 0.05). No other significant differences were measured. In conclusion a single reapplication of silane maintained the bond strength of resin to porcelain when final cementation was preceded by a try-in procedure and cleaning.[1]

References

Shear bond strength of resin bonded ceramic after different try-in procedures. Della Bona, A., Northeast, S.E. Journal of dentistry. (1994) [Pubmed]

Annotations and hyperlinks in this abstract are from individual authors of WikiGenes or automatically generated by the WikiGenes Data Mining Engine. The abstract is from MEDLINE®/PubMed®, a database of the U.S. National Library of Medicine.About WikiGenes Open Access Licence Privacy Policy Terms of Use apsburg

The world's first wiki where authorship really matters (Nature Genetics, 2008). Due credit and reputation for authors. Imagine a global collaborative knowledge base for original thoughts. Search thousands of articles and collaborate with scientists around the globe.